Introduction
Ariaperse dyes can be used for dyeing and printing polyester, acetate, triacetate, nylon and acrylic. The colur shade card contains information on various properties of application
Ariaperse dyes are eminently used for making self shade as well as compound ones. They provide high tinctorial power, good leveling effect and favourable reproducibility for dyeing and printing
:Ariaperse dyes can be classified into the following three groups
(E) Subzero type: Dyes which show excellent leveling property and are applied mainly to high temperature and
(SE) Medium temperature type: Dyes which show high fastness properties, especialy light fastness and are applied to any dyeing process
(S) High temperature type: Dyes which show excellent sublimation fastness and can sufficiently atand hard treatment process after dyeing, such as pleat and permanent press finishing. They are applied mainly to high temperature dyeing, themosol dyeing and printing. Finally, dyes of our corporation are a series of disperse dyes which have been marketed for synthetic fibers, especialy polyester fibers
Dyeing methods
High temperature dyeing method *
A. Dyes :x% (o.w.f)
B. Leveling agent :0.5-1g/l
C. PH : PH 4.5-5 (adjusted with acetic acid 0.25 g/l and sodium acetate 1g/l)
Temp.,Time : Riase the temperature from 90c to 130c in 30-50 min and dye for 30-50 min at 130c
Liquor ratio : 1:10~30
Reduction clearing :Hydrousulfite cc.1g/l
Naoh (40 BE)2 m/l
Nonionic surfactant 1 g/l
Liqour ratio1:30
Temp,Time 85c X 10min
Dyeing procedure
Carrier dyeing method *
A.Dyes : x % (o.w.f)
B.Carrier : Carrier P cone 4g/l
C.PH : PH 4.5-5 (adjusted with acetic acid 0.25 g/l and sodium acetate 1 g/l)
Temp, Time : Raise the temperature from 50c to 100 c in 30 min and dye at the boil for 60-90 min
Others : Same as in high temperature dyeing
Printing method *
Material : Polyester fabric
Printing paste: Disperse dyes xg
Water : 250g
Stock Thickening (locust bean gum type) 550 g
reduction : 2 g
inhibitor (sodium chlorate)
Tartaric acid : 3 g
Balance (water or thickener) : y g
Total : 1000 g
For reduction printing depth, the above printing paste is mixed to the following reducing thickening
Reducting : Stock thickening 700 g
Thickening : Water 293 g
Reduction inhibitor 4 g
Tartaric acid 3 g
Total 1000 g
Proced: Printing → Drying → H.P.Steaming (130 c × 30min) → Rinsing → Reduction clearing → Rinsing → Dryeing
Thermosol dyeing method *
Material : Polyester fabric
Dyeing depth : X g/l
Migration inhibitor Sodium alginate 1 g/l
Proced : Preparation of padding liquor → Padding → ureSqueezing (Pick-up 60-70%) → Intermediate drying (110 c × 60 sec) → Thermosoling (180 c ~ 220 c × 90sec) → Rinsing → Reduction clearing → Rinsing → Drying
Test method of physical properties
Light: Iso – 105/BO2
Wahsing : Iso – 105/CO3
Rubbing: Iso – 105/X12
Sublimatio: Iso – 105/POI
Perspiratio: Iso – 105/EO4
For reference only
Note
Very Suitable ○ Sutiable Δ Less Suitable X Not
DISPERSE ARIAPERS DYES |
PRODUCT NAME | FASTNESS & DYEING PROPERTIES | |||||||||||||||||
C.I.NO | LIGHT(1/1) | SUBLIMATION | WASHING | WASHING PERSPIRATION | RUBBING (DRY) | EXHAUST | THEROSOL | MICRO FIBER |
PRINTING | DISCHARGE | CARRIER | APPLICABLE RANGE OF PH |
LEVELING PROPERTY |
||||||
STANING ON NYLON | STANING ON ACETATE |
STANING ON ACETATE |
STANING ON POLYSTER |
||||||||||||||||
Applications HIGH TEMP DYES(HT) |
|||||||||||||||||||
0/5gr/kg | 2gr/kg | ||||||||||||||||||
YELLOW 4GNL 200% | * | 7 | 4 | 4 .5 | 4 . 5 | 4 . 5 | 4 . 5 | 5 | 5 | ● | ○ | ● | ▲ | × | ▲ | 3 . 7 | SE | ||
YELLOW 3GE 200% | Y-54 | 7 | 4 | 5 | 4 | 4 . 5 | 5 | 4 . 5 | 5 | ● | ▲ | ○ | ▲ | × | ● | 2 . 9 | E | ||
YELLOW 3G 200% | * | 7 | 4 | 4 . 5 | 4 . 5 | 4 . 5 | 5 | 5 | 5 | ● | ○ | ● | ▲ | × | ▲ | 3 . 7 | SE | ||
YELLOW ER |
* | 6 . 7 | 4 | 4 . 5 | 4 . 5 | 4 . 5 | 4 . 5 | 4 . 5 | 4 . 5 | ● | × | ● | × | × | ○ | 3 . 7 | SE | ||
ORANGE 3RL | O-25 | 6 | 4 | 5 | 4 | 4 . 5 | 4 . 5 | 5 | 4 . 5 | ● | ▲ | × | × | × | ● | 2 . 9 | SE | ||
SCARLET GSL 200% | R-153 | 6 | 4 . 5 | 5 | 5 | 5 | 5 | 4 . 5 | 5 | ● | ○ | ○ | ● | ● | ▲ | 2 . 10 | SE | ||
RED FBL 200% | R-60 | 6 | 3 | 5 | 4 . 5 | 4 . 5 | 5 | 4 . 5 | 5 | ● | ▲ | ○ | × | × | ● | 2 . 9 | E | ||
RED BL 200% | * | 5 | 3 | 4 . 5 | 4 . 5 | 4 | 4 . 5 | 4 | 4 . 5 | ● | ○ | ▲ | ● | ● | × | 3 . 8 | SE | ||
RED BS 200% | R-152 | 6 | 4 . 5 | 5 | 5 | 5 | 5 | 4 . 5 | 5 | ● | ● | ○ | ● | ● | ▲ | 2 . 9 | SE | ||
RUBINE 3GLS 200% | R-73 | 6 | 4 . 5 | 5 | 4 . 5 | 4 | 5 | 4 . 5 | 4 . 5 | ● | ○ | ○ | ○ | ● | ○ | 2 . 8 | SE | ||
BROWN PNR | * | 5 . 6 | 4 . 5 | 5 | 5 | 5 | 5 | 4 . 5 | 5 | ● | ○ | × | ○ | ▲ | × | 3 . 7 | SE | ||
BROWN 2BL | * | 5 . 6 | 4 . 5 | 4 . 5 | 4 . 5 | 5 | 4 . 5 | 4 . 5 | 4 . 5 | ● | ○ | ▲ | × | × | ○ | 3 . 7 | SE | ||
TUR.BLUE SG 200% | * | 6 | 4 . 5 | 4 . 5 | 4 | 4 . 5 | 5 | 5 | 5 | ● | ● | × | ● | × | ▲ | 3 . 9 | S | ||
BLUE EBL | B.56 | 6 . 7 | 3 . 4 | 4 . 5 | 4 . 5 | 4 . 5 | 5 | 4 . 5 | 4 . 5 | ● | ▲ | ● | ▲ | × | ● | 2 . 9 | E | ||
BLUE BL | * | 6 | 4 | 5 | 5 | 5 | 5 | 4 . 5 | 4 . 5 | ● | ○ | ○ | ○ | × | ○ | 3 . 7 | SE | ||
BLUE 2RL | B.183:1 | 5 . 6 | 4 | 5 | 5 | 5 | 5 | 4 . 5 | 4 . 5 | ● | ○ | ○ | ○ | × | ○ | 3 . 7 | SE | ||
NAVY BLUE SGL 200% | B.79 | 5 . 6 | 4 . 5 | 5 | 4 | 4 . 5 | 5 | 5 | 5 | ● | ● | × | ● | × | × | 3 . 6 | S | ||
NAVYBLUEEXSF 300% | * | 5 . 6 | 4 | 4 | 5 | 4 . 5 | 4 . 5 | 4 . 5 | 4 . 5 | ● | ▲ | × | ▲ | × | ▲ | 2 . 9 | SE | ||
BLACK RD3G 400(1-4)% | * | 5 . 6 | 4 | 5 | 4 . 5 | 4 . 5 | 5 | 4 | 4 . 5 | ● | ○ | × | ▲ | × | ▲ | 2 . 9 | SE |
DISPERSE ARIAPERSE DYES |
PRODUCT NAME | FASTNESS & DYEING PROPERTIES | |||||||||||||||||
C.I.NO | LIGHT(1/1) | SUBLIMATION | WASHING | WASHING PERSPIRATION | RUBBING (DRY) | EXHAUST | THEROSOL | MICRO FIBER |
PRINTING | DISCHARGE | CARRIER | APPLICABLE RANGE OF PH |
LEVELING PROPERTY |
||||||
STANING ON NYLON | STANING ON ACETATE |
STANING ON ACETATE |
STANING ON POLYSTER |
||||||||||||||||
Applications LUMINOUS DYES |
|||||||||||||||||||
0/5gr/kg | 2gr/kg | ||||||||||||||||||
|
FLOU.YELLOW10GF | * | 4 | 5 | 4 . 5 | 4 | 4 | 4 . 5 | 5 | 4 | ● | ● | × | ● | × | × | 3 . 7 | SE | |
|
FLOU.RED2GL | * | 4 | 4 . 5 | 5 | 4 . 5 | 4 . 5 | 4 . 5 | 4 | 4 | ● | ● | × | ● | × | × | 3 . 7 | S | |
|
LUMINOUSRED G | * | 4 | 5 | 5 | 5 | 5 | 5 | 4 . 5 | 4 . 5 | ● | ● | × | ● | × | × | 3 .7 | S | |
|
TUR.BLUE BG 200% | * | 6 . 7 | 4 . 5 | 5 | 5 | 5 | 5 | 5 | 5 | ● | ● | ○ | ● | × | ○ | 3 . 8 | S |
DISPERSE ARIAPERSE DYES |
PRODUCT NAME | FASTNESS & DYEING PROPERTIES | |||||||||||||||||
C.I.NO | LIGHT(1/1) | SUBLIMATION | WASHING | WASHING PERSPIRATION | RUBBING (DRY) | EXHAUST | THEROSOL | MICRO FIBER |
PRINTING | DISCHARGE | CARRIER | APPLICABLE RANGE OF PH |
LEVELING PROPERTY |
||||||
STANING ON NYLON | STANING ON ACETATE |
STANING ON ACETATE |
STANING ON POLYSTER |
||||||||||||||||
Applications LOW TEMP DYES(CARRIER) |
|||||||||||||||||||
0/5gr/kg | 2gr/kg | ||||||||||||||||||
YELLOW GE 200% | * | 7 | 4 | 5 | 4 | 4 . 5 | 5 | 4 . 5 | 5 | ● | ▲ | ○ | ▲ | × | ● | 2 . 9 | E | ||
RED BLE 200% | * | 6 | 3 | 5 | 4 . 5 | 4 . 5 | 5 | 4 . 5 | 5 | ● | ▲ | ○ | × | × | ● | 2 . 9 | E | ||
BLUE BLE | * | 6 . 7 | 3 . 4 | 4 . 5 | 4 . 5 | 4 . 5 | 5 | 4 . 5 | 4 . 5 | ● | ▲ | ● | ▲ | × | ● | 2 . 9 | E | ||
BLACK CR(1-4)% | * | 5 . 6 | 4 | 5 | 5 | 5 | 5 | 4 . 5 | 4 . 5 | ● | × | ○ | × | × | ● | 3 . 8 | E |
DISPERSE ARIAPERSE DYES |
PRODUCT NAME | FASTNESS & DYEING PROPERTIES | |||||||||||||||||
C.I.NO | LIGHT(1/1) | SUBLIMATION | WASHING | WASHING PERSPIRATION | RUBBING (DRY) | EXHAUST | THEROSOL | MICRO FIBER |
PRINTING | DISCHARGE | CARRIER | APPLICABLE RANGE OF PH |
LEVELING PROPERTY |
||||||
STANING ON NYLON | STANING ON ACETATE |
STANING ON ACETATE |
STANING ON POLYSTER |
||||||||||||||||
Applications PRINTING & THERMOSOL |
|||||||||||||||||||
0/5gr/kg | 2gr/kg | ||||||||||||||||||
YELLOW GFS | * | 6 . 7 | 4 . 5 | 5 | 4 . 5 | 4 . 5 | 5 | 4 . 5 | 4 . 5 | ● | ● | ○ | ● | ● | ▲ | 2 . 7 | S | ||
RED TBLS 200% | * | 6 | 4 . 5 | 5 | 4 . 5 | 4 . 5 | 5 | 4 . 5 | 4 . 5 | ● | ● | ○ | ● | × | × | 2 . 9 | SE | ||
RED FTS | * | 6 | 5 | 5 | 4 . 5 | 4 . 5 | 5 | 4 . 5 | 5 | ● | ○ | ○ | ● | ○ | ▲ | 3 . 8 | S | ||
RUBINE S2GFL | * | 6 . 7 | 5 | 5 | 4 . 5 | 5 | 5 | 4 | 4 . 5 | ● | ● | ● | ● | × | × | 3 . 7 | S | ||
BLUE BBLS 200% | * | 6 | 4 . 5 | 4 . 5 | 4 | 4 . 5 | 5 | 5 | 5 | ● | ● | × | ● | × | ▲ | 3 . 9 | S | ||
N.BLUE MRD | * | 5 . 6 | 4 . 5 | 5 | 4 | 4 . 5 | 5 | 5 | 5 | ● | ● | × | ● | × | × | 3 . 6 | S | ||
Y.BROWN RLS 150% | * | 6 | 5 | 4 . 5 | 5 | 5 | 5 | 5 | 5 | ● | ● | × | ● | ● | ○ | 3 . 7 | S | ||
BROWN RMD | * | 6 | 5 | 4 . 5 | 5 | 5 | 5 | 4 . 5 | 5 | ○ | ● | × | ● | × | × | 3 . 7 | S | ||
BROWN GMD | * | 6 | 5 | 4 . 5 | 5 | 5 | 5 | 4 . 5 | 5 | ○ | ● | × | ● | × | × | 3 . 7 | S | ||
GRAY MD | * | 5 6 | 5 | 5 | 5 | 4 . 5 | 5 | 5 | 5 | × | ● | × | ● | × | ▲ | 3 . 6 | S | ||
BLACK AMRD(1-4)% | * | 5 . 6 | 5 | 5 | 5 | 4 . 5 | 5 | 5 | 5 | × | ● | × | ● | × | ▲ | 3 . 6 | S | ||
BLACK BNFS 200(1-4)% | * | 6 | 5 | 5 | 4 . 5 | 4 . 5 | 5 | 4 . 5 | 4 | ● | ● | × | ● | × | ▲ | 3 . 7 | S |